Kuyimitsa ndi kuzimitsa ndi kukalamba ndi mitundu yoyambira yochizira kutentha ya ma aluminiyamu aloyi. Annealing ndi chithandizo chofewa, chomwe cholinga chake ndi kupanga yunifolomu ya alloy ndi yokhazikika muzolemba ndi mapangidwe, kuthetsa kuuma kwa ntchito, ndi kubwezeretsa pulasitiki ya alloy. Kuzimitsa ndi kukalamba ndi kulimbikitsa kutentha mankhwala, cholinga chake ndi kupititsa patsogolo mphamvu ya aloyi, ndipo makamaka ntchito zotayidwa aloyi kuti akhoza kulimbikitsidwa ndi kutentha mankhwala.
1 Kusintha
Malingana ndi zofunikira zosiyanasiyana zopanga, aluminium alloy annealing imagawidwa m'njira zingapo: ingot homogenization annealing, billet annealing, intermediate annealing ndi kumaliza mankhwala annealing.
1.1 Ingot homogenization annealing
Pansi pamikhalidwe ya condensation yofulumira komanso yosagwirizana ndi crystallization, ingot iyenera kukhala ndi mawonekedwe osagwirizana ndi kapangidwe kake, komanso kukhala ndi nkhawa yayikulu mkati. Kuti musinthe izi ndikuwongolera magwiridwe antchito a ingot, homogenization annealing nthawi zambiri imafunika.
Pofuna kulimbikitsa kufalikira kwa atomiki, kutentha kwapamwamba kuyenera kusankhidwa kuti pakhale homogenization annealing, koma sikuyenera kupitirira malo otsika osungunuka a eutectic osungunuka a alloy. Nthawi zambiri, kutentha kwa annealing homogenization ndi 5 ~ 40 ℃ kutsika kuposa malo osungunuka, ndipo nthawi yocheperako imakhala pakati pa 12 ~ 24h.
1.2 Billet annealing
Billet annealing imatanthawuza kutsekeka kusanayambike kuzizira koyambirira panthawi yakukakamiza. Cholinga chake ndikupangitsa kuti billet ipeze dongosolo loyenera komanso kukhala ndi mphamvu zambiri zowonongeka za pulasitiki. Mwachitsanzo, kutentha kozungulira kwa aluminium alloy slab ndi 280 ~ 330 ℃. Pambuyo kuzirala mofulumira kutentha firiji, ntchito kuumitsa chodabwitsa sangathe kutheratu. Makamaka, chifukwa cha kutentha kwazitsulo zotayidwa zolimbitsa thupi, pambuyo pozizira mofulumira, ndondomeko ya recrystallization siinathe, ndipo njira yolimba ya supersaturated sichinawonongeke kwathunthu, ndipo gawo lina la ntchito yowumitsa ndi kuzimitsa limasungidwabe. Ndikovuta kuziziritsa molunjika popanda kutsekereza, chifukwa chake ndikofunikira kuti billet annealing. Kwa ma aluminiyamu olimba osatenthedwa, monga LF3, kutentha kwa annealing ndi 370 ~ 470 ℃, ndipo kuziziritsa kwa mpweya kumachitika mukatentha kwa 1.5 ~ 2.5h. Kutentha kwa billet ndi annealing komwe kumagwiritsidwa ntchito pokonza chubu chozizira kuyenera kukhala kokwera moyenerera, ndipo kutentha kwapamwamba kumatha kusankhidwa. Kwa ma aluminiyamu omwe amatha kulimbikitsidwa ndi kutentha, monga LY11 ndi LY12, kutentha kwa billet annealing ndi 390 ~ 450 ℃, kusungidwa pa kutentha kumeneku kwa 1 ~ 3h, kenako kuzirala mu ng'anjo mpaka pansi pa 270 ℃ pa mlingo wosapitirira 30 ℃ / h ndi ng'anjo yotuluka mumlengalenga.
1.3 Kusintha kwapakati
Wapakatikati annealing amatanthauza annealing pakati ozizira mapindikidwe njira, cholinga chake ndi kuthetsa ntchito kuumitsa kuti atsogolere kupitiriza ozizira mapindikidwe. Nthawi zambiri, zinthuzo zitatsekedwa, zimakhala zovuta kupitiliza kugwira ntchito mozizira popanda kutsekereza kwapakatikati mutatha kuzizira kwa 45-85%.
Kachitidwe ka annealing wapakatikati kwenikweni ndi wofanana ndi wa billet annealing. Malinga ndi zofunikira za digiri ya deformation yozizira, annealing wapakatikati akhoza kugawidwa m'magulu atatu: annealing wathunthu (total deformation ε≈60 ~ 70%), annealing yosavuta (ε≤50%) ndi annealing pang'ono (ε≈30 ~ 40%). Njira ziwiri zoyambilira za annealing ndi zofanana ndi billet annealing, ndipo chomalizacho chimatenthedwa pa 320 ~ 350 ℃ kwa 1.5 ~ 2h kenako mpweya utakhazikika.
1.4. Anamaliza mankhwala annealing
Kutsirizitsa mankhwala annealing ndi kutentha komaliza komwe kumapereka zinthu zina zamagulu ndi zamakina malinga ndi zofunikira zaukadaulo wazinthu.
Anamaliza mankhwala annealing akhoza kugawidwa mu kutentha annealing (kupanga zinthu zofewa) ndi otsika kutentha annealing (kupanga mankhwala theka-zovuta m'mayiko osiyanasiyana). Kutentha kwapamwamba kuyenera kuonetsetsa kuti mawonekedwe athunthu a recrystallization ndi pulasitiki wabwino angapezeke. Pansi pa chikhalidwe chowonetsetsa kuti zinthuzo zimapeza mapangidwe abwino ndi ntchito, nthawi yogwira sikuyenera kukhala yaitali kwambiri. Pakuti zotayidwa aloyi kuti akhoza kulimbikitsidwa ndi kutentha mankhwala, pofuna kupewa mpweya kuzirala quenching tingati kuzirala mlingo ayenera mosamalitsa.
Kuchepetsa kutentha kumaphatikizapo kuchepetsa kupsinjika ndi kufewetsa pang'ono, komwe kumagwiritsidwa ntchito makamaka ngati aluminiyamu yoyera komanso mankhwala osatentha omwe amalimbitsa ma aluminiyamu. Kupanga otsika kutentha annealing dongosolo ndi ntchito yovuta kwambiri, amene osati ayenera kuganizira kutentha annealing ndi kusunga nthawi, komanso ayenera kuganizira mphamvu ya zonyansa, alloying digiri, ozizira deformation, wapakatikati annealing kutentha ndi kutentha deformation kutentha. Kupanga otsika kutentha annealing dongosolo, m'pofunika kuyeza kusintha pamapindikira pakati kutentha annealing ndi makina katundu, ndiyeno kudziwa annealing kutentha osiyanasiyana malinga ndi zizindikiro ntchito zotchulidwa mikhalidwe luso.
2 Kuzimitsa
Kuzimitsidwa kwa zotayidwa aloyi amatchedwanso njira mankhwala, amene ndi kupasuka zinthu zambiri aloyi mu zitsulo monga gawo lachiwiri mu njira olimba monga nkotheka kudzera mkulu-kutentha Kutentha, kenako kuzirala mofulumira ziletsa mpweya wa gawo lachiwiri, potero kupeza supersaturated zotayidwa ofotokoza α olimba njira, amene ali bwino kukonzekera lotsatira kukalamba.
Mfundo yopezera yankho lolimba la supersaturated α ndiloti kusungunuka kwa gawo lachiwiri mu alloy mu aluminiyamu kuyenera kuwonjezeka kwambiri ndi kuwonjezeka kwa kutentha, mwinamwake, cholinga cha chithandizo cholimba sichingakwaniritsidwe. Zinthu zambiri zopangira ma aluminiyamu zimatha kupanga chithunzi cha eutectic ndi chikhalidwe ichi. Kutengera aloyi ya Al-Cu mwachitsanzo, kutentha kwa eutectic ndi 548 ℃, ndipo kutentha kwa chipinda chamkuwa mu aluminiyamu kumakhala kosakwana 0.1%. Mukatenthedwa mpaka 548 ℃, kusungunuka kwake kumawonjezeka mpaka 5.6%. Choncho, ma aloyi a Al-Cu omwe ali ndi mkuwa wosakwana 5.6% amalowa m'chigawo cha α chimodzi pambuyo pa kutentha kwa kutentha kupitirira mzere wake wa solvus, ndiko kuti, gawo lachiwiri la CuAl2 limasungunuka kwathunthu mu matrix, ndipo yankho limodzi la supersaturated α likhoza kupezedwa pambuyo pozimitsa.
Kuzimitsa ndiye ntchito yofunika kwambiri komanso yofunika kwambiri yochizira kutentha kwa ma aluminiyamu. Chinsinsi ndi kusankha yoyenera quenching Kutentha kutentha ndi kuonetsetsa zokwanira quenching kuzirala mlingo, ndi mosamalitsa kulamulira ng'anjo kutentha ndi kuchepetsa quenching mapindikidwe.
Mfundo yosankha kutentha kozimitsa ndikuwonjezera kutentha kwa kutentha kozimitsa momwe mungathere ndikuwonetsetsa kuti aloyi ya aluminiyamu sichiwotcha kwambiri kapena mbewu zimakula mopitirira muyeso, kuti muwonjezere supersaturation ya α yankho lolimba ndi mphamvu pambuyo pokalamba mankhwala. Nthawi zambiri, ng'anjo yotenthetsera ya aluminiyamu imafuna kuwongolera kutentha kwa ng'anjo kukhala mkati mwa ± 3 ℃, ndipo mpweya wa ng'anjo umakakamizika kuzungulira kuti zitsimikizire kutentha kwa ng'anjo.
Kuwotcha kwambiri kwa aloyi ya aluminiyamu kumayamba chifukwa cha kusungunuka kwapang'ono kwa zigawo zotsika zosungunuka mkati mwachitsulo, monga ma binary kapena ma eutectics ambiri. Kuwotcha mopitirira muyeso sikungoyambitsa kuchepetsa mphamvu zamakina, komanso kumakhudza kwambiri kukana kwa dzimbiri kwa alloy. Choncho, pamene aloyi ya aluminiyamu yatenthedwa, sichikhoza kuthetsedwa ndipo mankhwala a alloy ayenera kuchotsedwa. Kutentha kwenikweni kwa aluminium alloy kumatsimikiziridwa makamaka ndi kaphatikizidwe ka aloyi ndi zonyansa, komanso kumagwirizana ndi kukonzanso kwa alloy. Kutentha kwambiri kwa zinthu zomwe zakhala zikupangidwanso ndi pulasitiki yopindika ndizokwera kuposa za castings. Kuchulukitsitsa kosinthika, kumakhala kosavuta kuti zigawo zotsika zosungunuka zisungunuke mu matrix zikatenthedwa, ndiye kuti kutentha kwenikweni kumawonjezeka.
Kuzizira kozizira pakuzimitsidwa kwa aloyi ya aluminiyamu kumakhudza kwambiri mphamvu yolimbitsa ukalamba komanso kukana kwa dzimbiri kwa aloyi. Panthawi yozimitsa LY12 ndi LC4, ndikofunikira kuwonetsetsa kuti njira yolimba ya α siyiwola, makamaka m'dera lomwe limakhudzidwa ndi kutentha kwa 290 ~ 420 ℃, komanso kuziziritsa kwakukulu kokwanira kumafunika. Nthawi zambiri zimanenedwa kuti kuzizira kuyenera kukhala pamwamba pa 50 ℃/s, ndipo pa aloyi ya LC4, iyenera kufika kapena kupitirira 170 ℃/s.
Njira yozimitsira yomwe imagwiritsidwa ntchito kwambiri pazitsulo za aluminiyamu ndi madzi. Zochita zopanga zikuwonetsa kuti kuzizira kwambiri pakuzimitsa, kumapangitsanso kupsinjika kotsalira ndikusintha kotsalira kwa zinthu zomwe zazimitsidwa kapena chogwirira ntchito. Chifukwa chake, pazigawo zing'onozing'ono zokhala ndi mawonekedwe osavuta, kutentha kwamadzi kumatha kutsika pang'ono, nthawi zambiri 10 ~ 30 ℃, ndipo sayenera kupitilira 40 ℃. Pakuti workpieces ndi akalumikidzidwa zovuta ndi kusiyana lalikulu makulidwe khoma, pofuna kuchepetsa quenching deformation ndi akulimbana, kutentha madzi nthawi zina ziwonjezeke kwa 80 ℃. Komabe, ziyenera kunenedwa kuti pamene kutentha kwa madzi a thanki yozimitsira kumawonjezeka, mphamvu ndi kukana kwa dzimbiri kwa zinthuzo kumachepetsanso moyenerera.
3. Kukalamba
3.1 Kusintha kwa bungwe ndi kusintha kwa machitidwe akamakalamba
The supersaturated α olimba njira yopezedwa ndi quenching ndi wosakhazikika dongosolo. Ikatenthedwa, imawola ndikusintha kukhala yofanana. Kutenga aloyi ya Al-4Cu mwachitsanzo, mawonekedwe ake ofanana ayenera kukhala α + CuAl2 (θ gawo). Pamene gawo limodzi la supersaturated α yankho lolimba pambuyo pozimitsa limatenthedwa chifukwa cha ukalamba, ngati kutentha kuli kokwanira, gawo la θ lidzawomberedwa mwachindunji. Kupanda kutero, zidzachitika pang'onopang'ono, ndiye kuti, pakadutsa magawo apakati, gawo lomaliza la CuAl2 litha kufikika. Chithunzi chomwe chili pansipa chikuwonetsa mawonekedwe a kristalo pagawo lililonse lamvula panthawi yokalamba ya Al-Cu alloy. Chithunzi a. ndi mawonekedwe a crystal lattice mu chikhalidwe chozimitsidwa. Panthawiyi, ndi gawo limodzi la α supersaturated olimba njira, ndipo maatomu amkuwa (madontho akuda) amagawidwa mofanana komanso mwachisawawa mu aluminiyamu (madontho oyera) matrix lattice. Chithunzi b. akuwonetsa kapangidwe ka latisi koyambirira kwa mvula. Ma atomu amkuwa amayamba kukhazikika m'malo ena a matrix lattice kuti apange dera la Guinier-Preston, lotchedwa GP area. Chigawo cha GP ndi chaching'ono kwambiri komanso chofanana ndi disc, chokhala ndi mainchesi pafupifupi 5 ~ 10μm ndi makulidwe a 0.4 ~ 0.6nm. Chiwerengero cha GP zone mu matrix ndi yayikulu kwambiri, ndipo kachulukidwe kagawidwe kamafikira 10¹⁷~10¹⁸cm-³ . Mapangidwe a kristalo a GP zone akadali ofanana ndi a matrix, onse ali ndi nkhope ya cubic, ndipo amasunga mawonekedwe ogwirizana ndi matrix. Komabe, chifukwa kukula kwa maatomu amkuwa n’kochepa poyerekezera ndi maatomu a aluminiyamu, kukhathamiritsa kwa maatomu amkuwa kumapangitsa kuti kristalo wa kristalo womwe uli pafupi ndi chigawocho ufooke, zomwe zimapangitsa kuti maatomuwo asokonezeke.
Chithunzi chojambula cha mawonekedwe a kristalo amasintha a Al-Cu alloy pakukalamba
Chithunzi a. Dziko lozimitsidwa, gawo limodzi α yankho lolimba, maatomu amkuwa (madontho akuda) amagawidwa mofanana;
Chithunzi b. Kumayambiriro kwa ukalamba, malo a GP amapangidwa;
Chithunzi c. Kumapeto kwa ukalamba, gawo losinthika lokhazikika limapangidwa;
Chithunzi d. Kutentha kwakukulu kukalamba, mpweya wa gawo losagwirizana
Malo a GP ndiye chinthu choyamba chomwe chimatulutsa mpweya chisanakwane chomwe chimawoneka pakakalamba kazitsulo zotayidwa. Kukulitsa nthawi yokalamba, makamaka kuonjezera kutentha kwa ukalamba, kudzapanganso magawo ena apakati. Mu aloyi ya Al-4Cu, pali θ "ndi θ 'magawo pambuyo pa GP zone, ndipo pamapeto pake gawo lofanana la CuAl2 lifikira. θ" ndi θ' onse ndi magawo osinthika a gawo la θ, ndipo mawonekedwe a kristalo ndi latisi lalikulu, koma chokhazikika cha latisi ndi chosiyana. Kukula kwa θ ndikokulirapo kuposa komweko kwa GP, komwe kumakhala ngati diski, komwe kumakhala pafupifupi 15 ~ 40nm ndi makulidwe a 0.8 ~ 2.0nm. Imapitilizabe kukhala ndi mawonekedwe ogwirizana ndi matrix, koma kuchuluka kwa kupotoza kwa lattice kumakhala kokulirapo. Pamene mukusintha kuchoka ku θ” kupita ku θ' gawo, kukula kwakula mpaka 20 ~ 600nm, makulidwe ake ndi 10 ~ 15nm, ndipo mawonekedwe ogwirizana amawonongekanso pang'ono, kukhala mawonekedwe osakanikirana, monga momwe tawonetsera pa Chithunzi c. mawonekedwe osagwirizana, monga momwe tawonetsera pa Chithunzi d.
Malinga ndi zomwe zili pamwambazi, dongosolo la ukalamba la mpweya wa Al-Cu alloy ndi αs→α+GP zone→α+θ”→α+θ'→α+θ. Gawo la ukalamba limadalira kapangidwe ka aloyi ndi kukalamba.
Panthawi yokalamba, gawo la GP ndi gawo losinthira lomwe limapangidwa kuchokera ku matrix ndi laling'ono, lomwazika kwambiri, komanso losapunduka mosavuta. Panthawi imodzimodziyo, zimayambitsa kusokonezeka kwa lattice mu masanjidwewo ndikupanga malo opsinjika, omwe amalepheretsa kwambiri kuyenda kwa ma dislocation, potero kumawonjezera kukana kwa mapindidwe a pulasitiki a aloyi ndikuwongolera mphamvu ndi kuuma kwake. Kuumitsa kukalamba kumeneku kumatchedwa kuuma kwa mvula. Chithunzi chomwe chili pansipa chikuwonetsa kusintha kwa kuuma kwa Al-4Cu alloy panthawi yozimitsa ndi kukalamba mankhwala mwa mawonekedwe a curve. Gawo I pachithunzichi likuyimira kuuma kwa aloyi mu chikhalidwe chake choyambirira. Chifukwa cha mbiri yakale yotentha yogwira ntchito, kuuma kwa chikhalidwe choyambirira kumasiyana, nthawi zambiri HV=30~80. Pambuyo pa kutentha pa 500 ℃ ndikuzimitsa (siteji II), maatomu onse amkuwa amasungunuka mu matrix kuti apange gawo limodzi la supersaturated α yankho lolimba ndi HV=60, lomwe ndi lolimba kuwirikiza kawiri kuposa kuuma kwa annealed state (HV=30). Izi ndi zotsatira za kulimbitsa yankho lolimba. Pambuyo pozimitsa, imayikidwa kutentha, ndipo kuuma kwa alloy kumawonjezeka mosalekeza chifukwa cha kupangika kosalekeza kwa madera a GP (gawo III). Kuumitsa kukalamba kumeneku kutentha kwa chipinda kumatchedwa kukalamba kwachilengedwe.
I—dziko loyambirira;
II-solid solution state;
III-kukalamba kwachilengedwe (GP zone);
IVa - chithandizo cha regression pa 150 ~ 200 ℃ (yosungunukanso mu GP zone);
IVb—kukalamba kochita kupanga (θ”+θ' gawo);
V—kuchuluka (θ”+θ' gawo)
Mu gawo la IV, alloy imatenthedwa mpaka 150 ° C chifukwa cha ukalamba, ndipo kuuma kwake kumakhala koonekeratu kuposa kukalamba kwachilengedwe. Panthawiyi, mankhwala a mvula ndi gawo la θ, lomwe limakhala ndi mphamvu yolimbitsa kwambiri muzitsulo za Al-Cu. Ngati kutentha kwa ukalamba kumawonjezeka, kusintha kwa mpweya kumachoka ku θ "gawo kupita ku gawo la θ, kuuma kumachepa, ndipo kuuma kumachepa, kulowa gawo la V. Kutentha kulikonse komwe kumafuna kuti siteji ya V. Kutenthetsa kwa ukalamba kumatchedwa siteji ya V. gulu ili. Ngati kuuma kumafika pamlingo wovuta kwambiri womwe aloyi imatha kufikira atakalamba (ie, siteji ya IVb), kukalamba uku kumatchedwa kukalamba pachimake. Ngati nsonga ya kuuma kwambiri sikunafike, imatchedwa kukalamba kapena kukalamba kosakwanira. Ngati mtengo wapamwamba wadutsa ndipo kuuma kumachepa, kumatchedwa kukalamba. Kukhazikika kwamankhwala okalamba kumakhalanso kwa kukalamba kwambiri. Malo a GP opangidwa panthawi ya ukalamba wachilengedwe ndi osakhazikika. Ikatenthedwa kwambiri kutentha kwambiri, monga pafupifupi 200 ° C, ndikutentha kwakanthawi kochepa, GP zone imasungunukanso mu njira yolimba ya α. Ngati itazimitsidwa mofulumira (kuzimitsidwa) musanayambe magawo ena osinthika monga θ" kapena θ' precipitate, aloyi ikhoza kubwezeretsedwa ku chikhalidwe chake choyambirira chozimitsidwa. Chodabwitsachi chimatchedwa "regression", ndiko kutsika kwamphamvu komwe kumasonyezedwa ndi mzere wa madontho mu siteji IVa mu chithunzi.
Kuumitsa zaka ndiye maziko opangira ma aluminiyamu ochiritsira kutentha, ndipo kuthekera kwake koumitsa zaka kumakhudzana mwachindunji ndi kapangidwe ka aloyi ndi njira yochizira kutentha. Al-Si ndi Al-Mn ma aloyi a binary alibe mphamvu yowumitsa mvula chifukwa gawo lofananira limalowa mwachindunji panthawi ya ukalamba, ndipo ndi ma aluminiyamu osawotcha. Ngakhale ma aloyi a Al-Mg amatha kupanga madera a GP ndi magawo osinthika β', amangokhala ndi kuthekera koumitsa mvula mu ma alloys apamwamba kwambiri. Al-Cu, Al-Cu-Mg, Al-Mg-Si ndi Al-Zn-Mg-Cu alloys ali ndi mphamvu yowumitsa mvula m'madera awo a GP ndi magawo osinthika, ndipo panopa ndi machitidwe akuluakulu a alloy omwe amatha kutentha ndi kulimbikitsidwa.
3.2 Kukalamba Mwachilengedwe
Nthawi zambiri, ma aloyi a aluminiyamu omwe amatha kulimbikitsidwa ndi chithandizo cha kutentha amakhala ndi kukalamba kwachilengedwe pambuyo pozimitsa. Kulimbikitsa kukalamba kwachilengedwe kumachitika chifukwa cha GP zone. Kukalamba kwachilengedwe kumagwiritsidwa ntchito kwambiri mu aloyi a Al-Cu ndi Al-Cu-Mg. Kukalamba kwachilengedwe kwa Al-Zn-Mg-Cu alloys kumatenga nthawi yayitali, ndipo nthawi zambiri zimatenga miyezi ingapo kuti zifike pamtunda wokhazikika, kotero kuti dongosolo la ukalamba lachilengedwe siligwiritsidwa ntchito.
Poyerekeza ndi ukalamba wochita kupanga, pambuyo pa ukalamba wachilengedwe, mphamvu ya zokolola za alloy ndi yochepa, koma pulasitiki ndi kulimba zimakhala bwino, ndipo kukana kwa dzimbiri ndikwapamwamba. Mkhalidwe wa aluminiyumu yolimba kwambiri ya Al-Zn-Mg-Cu ndiyosiyana pang'ono. Kukana kwa dzimbiri pambuyo pa ukalamba wochita kupanga nthawi zambiri kumakhala bwino kuposa kukalamba kwachilengedwe.
3.3 Ukalamba Wopanga
Pambuyo pochiza ukalamba wochita kupanga, ma aloyi a aluminiyamu amatha kupeza mphamvu zokolola zambiri (makamaka kulimbitsa gawo la kusintha) komanso kukhazikika kwabungwe. Aluminiyamu yolimba kwambiri, aluminiyumu yopukutira ndi aluminiyamu yotayidwa amakhala okalamba kwambiri. Kutentha kwa ukalamba ndi nthawi yokalamba zimakhudza kwambiri katundu wa alloy. Kutentha kwa ukalamba nthawi zambiri kumakhala pakati pa 120 ~ 190 ℃, ndipo nthawi yokalamba sichidutsa 24h.
Kuphatikiza pa ukalamba wochita kupanga wagawo limodzi, ma aloyi a aluminiyamu amathanso kutengera dongosolo lokalamba lochita kupanga. Ndiko kuti, kutentha kumachitidwa kawiri kapena kuposa pa kutentha kosiyana. Mwachitsanzo, LC4 aloyi akhoza zaka 115 ~ 125 ℃ kwa 2 ~ 4h ndiyeno 160 ~ 170 ℃ kwa 3 ~ 5h. Kukalamba pang'onopang'ono sikungafupikitse nthawi, komanso kusintha ma microstructure a Al-Zn-Mg ndi Al-Zn-Mg-Cu, ndikuwongolera kwambiri kukana kwa dzimbiri, kutopa ndi kulimba kwa fracture popanda kwenikweni kuchepetsa makina.
Nthawi yotumiza: Mar-06-2025